Features
Proven Daubert Cromwell corrosion inhibitor chemistry
- Protects ferrous and non-ferrous metals
- Clings to metal surfaces
- Dry to the touch in 2-4 hours. Cures in 24 hours.
- Dried film is non-tacky, amber colored, wax-like and semi-transparent
- OEM Approved
- Compatible with Daubert Cromwell corrosion inhibitor papers, films and emitters
- Available in 5-gal drums, 55-gal. drums and totes.
Typical Applications
Transport, export, storage of metal products
- Hose fittings, connectors, and similar exposed areas
- Equipment, machinery, and components during overseas shipments
- Large metal parts stored outdoors
- Long-term indoor storage of metal parts, dies, tools, spares
- Castings and machined surfaces that cannot be protected from the elements
- Fabricated metal components and sub-assemblies
Surface Preparation and Application:
The metal surface should be clean, dry and free of rust, oil and mil scale. Metal temperature should be between 50-95°F (10-35°C) at the time of application. Apply by dip, brush or spray. Apply Nox-Rust 3100G 8-10 mils wet. The dry thickness will be 3.6-4.5 mils. The buildup of more than 6 mils is undesirable and not required.
When using an airless spray system, recommended equipment is a 15:1 or 23:1 type pump, a regulator, 25-or 50-ft. hose, and a P-500 type spray gun with a reversible tip. Tip size could range from 319-.321. Spray pressure is typically between 65-80 psi. The recommended starting point is 70 psi, and then adjust as operator determines is best for the application.
The curing process takes place by solvent evaporation. Allow adequate ventilation. Dry time will be affected by temperature and humidity. Typical dry-to-handle time is 2-4 hours, curing in 24 hours. The coating will have self-healing properties for up to 90 days.
Removal
Nox-Rust 3100G liquid can be removed from metal surfaces by most solvent borne thinners , by vapor degreasing , high press urehot alkaline wash, low pressure steam or using mineral spirits or kerosene –soaked towels.